TY - GEN N1 - Optica Applicata, Vol. 39, 2009, nr 4, s. 859-863 N2 - The primary crystallization of Co78Si9B13 metallic glass starts at 648 K and as a consequence of this the ε-Co(Si) phase with needle morphology is created. The second stage of crystallization (at 773 K) is the eutectic and as a result of this α-Co(Si) and boron phases: (Co,Si)3B, (Co,Si)2B are formed. The crystallites of these phases have layer morphology. These characteristic morphologies in the first and second stages lead to the increase in coercivity. L1 - http://dbc.wroc.pl/Content/62691/optappl_3904p859.pdf M3 - artykuł L2 - http://dbc.wroc.pl/Content/62691 PY - 2009 KW - optyka KW - metallic glass KW - crystallization KW - coercivity C1 - Wszystkie prawa zastrzeżone (Copyright) A1 - Jakubczyk, Ewa A1 - Lelątko, Józef A1 - Pawlik, Katarzyna A1 - Przybył, Anna A2 - Gaj, Miron. Redakcja A2 - Urbańczyk, Wacław. Redakcja PB - Oficyna Wydawnicza Politechniki Wrocławskiej C6 - Dla wszystkich w zakresie dozwolonego użytku LA - eng CY - Wrocław T1 - Influence of structural changes of Co78Si9B13 metallic glass on magnetic properties UR - http://dbc.wroc.pl/dlibra/publication/edition/62691 ER -