Problems with cracking of AlxGa1–x N layers

Tytuł publikacji grupowej:

Optica Applicata

Autor:

Dumiszewska, Ewa ; Lenkiewicz, Dariusz ; Strupiński, Włodzimierz ; Jasik, Agata ; Jakieła, Rafał S. ; Wesołowski, Marek

Współtwórca:

Gaj, Miron. Redakcja ; Wilk, Ireneusz. Redakcja

Temat i słowa kluczowe:

optyka ; Al0.4Ga0.6N ; GaN ; Si doping

Opis:

Optica Applicata, Vol. 35, 2005, nr 1, s. 111-115

Abstrakt:

AlxGa1–xN is a wide band-gap material, which can be used for manufacture of UV detectors. Unfortunately, there are problems with the cracking of those layers occurring above some critical thickness, which is a bit smaller from the one used for detectors (about 1 mm). Our investigation concentrated on the causes of crack formation. To avoid it we used so-called special AlN nucleation layer, which was to stop the relaxation. We obtained a strained layer free of cracking, but with a very big number of dislocations. We compared dislocation densities of strained and relaxed Al0.4Ga0.6N layers. The first one was characterized by a higher dislocation density than the second one. We also investigated the problem with cracking occurring in Al0.4Ga0.6N epitaxial layers during the doping, and how to control this process. The relaxation of the layers started for very low impurity densities and went on when we increased the amount of the dopant.

Wydawca:

Oficyna Wydawnicza Politechniki Wrocławskiej

Miejsce wydania:

Wrocław

Data wydania:

2005

Typ zasobu:

artykuł

Źródło:

<sygn. PWr A3481II> ; kliknij tutaj, żeby przejść ; kliknij tutaj, żeby przejść

Język:

eng

Powiązania:

Optica Applicata ; Optica Applicata, Vol. 35, 2005 ; Optica Applicata, Vol. 35, 2005, nr 1 ; Politechnika Wrocławska. Wydział Podstawowych Problemów Techniki

Prawa:

Wszystkie prawa zastrzeżone (Copyright)

Prawa dostępu:

Dla wszystkich w zakresie dozwolonego użytku

Lokalizacja oryginału:

Politechnika Wrocławska

×

Cytowanie

Styl cytowania: