Tytuł:

The evolution of microstructure in annealed LaFeSi-type alloys

Tytuł publikacji grupowej:

Optica Applicata

Autor:

Gębara, Piotr ; Pawlik, Piotr ; Kulej, Edyta ; Wysłocki, Jerzy J. ; Pawlik, Katarzyna ; Przybył, Anna

Współtwórca:

Gaj, Miron. Redakcja ; Urbańczyk, Wacław. Redakcja

Temat i słowa kluczowe:

optyka ; microstructure ; magnetocaloric materials ; X-ray diffraction

Opis:

Optica Applicata, Vol. 39, 2009, nr 4, s. 761-764

Abstrakt:

The evolution of microstructure and the phase constitution of the LaFe11.0Co0.8(Si0.4Al0.6)1.2 alloy in as-cast state and after subsequent annealing at 1323 K for 10, 20, 49 days was studied. In the LaFe11.0Co0.8(Si0.4 Al0.6)1.2 alloy after arc-melting, the dominant dendritic α-Fe phase crystallizes, which is confirmed by X-ray diffraction. Annealing of the samples resulted in evolution of microstructure and the phase constitution. Prolonged annealing of the samples causes almost full homogenization of the alloy with the single-phase structure identified as La(Fe0.85Co0.06Si0.04Al0.05)13 phase of the NaZn13-type structure.

Wydawca:

Oficyna Wydawnicza Politechniki Wrocławskiej

Miejsce wydania:

Wrocław

Data wydania:

2009

Typ zasobu:

artykuł

Źródło:

<sygn. PWr A3481II> ; kliknij tutaj, żeby przejść ; kliknij tutaj, żeby przejść

Język:

eng

Powiązania:

Optica Applicata ; Optica Applicata, Vol. 39, 2009 ; Optica Applicata, Vol. 39, 2009, nr 4 ; Politechnika Wrocławska. Wydział Podstawowych Problemów Techniki

Prawa:

Wszystkie prawa zastrzeżone (Copyright)

Prawa dostępu:

Dla wszystkich w zakresie dozwolonego użytku

Lokalizacja oryginału:

Politechnika Wrocławska