Transparent (1–x)TiO2–xFe2O3 (x = 0, 5, 10, 15 and 20 mol%) thin films prepared by sol-gel process

Tytuł publikacji grupowej:

Optica Applicata

Autor:

Hwang, Kyu-Seog ; Jeon, Young-Sun ; Jeon, Kyung-Ok ; Kim, Byung-Hoon

Współtwórca:

Gaj, Miron. Redakcja ; Wilk, Ireneusz. Redakcja

Temat i słowa kluczowe:

optyka ; titanium oxide ; thin film ; iron

Opis:

Optica Applicata, Vol. 35, 2005, nr 2, s. 191-199

Abstrakt:

Transparent iron-doped titanium oxide thin films were prepared on soda-lime-silica glass substrate from a titanium naphthenate precursor. Films prefired at 500°C for 10 min were finally annealed at 500°C for 30 min in air. Field emission–scanning electron microscope and scanning probe microscope were used for characterizing the surface structure of the film. A sharp absorption edge of the film was observed. The film containing iron showed a shift towards the visible in the absorption threshold.

Wydawca:

Oficyna Wydawnicza Politechniki Wrocławskiej

Miejsce wydania:

Wrocław

Data wydania:

2005

Typ zasobu:

artykuł

Format:

application/pdf

Źródło:

<sygn. PWr A3481II> ; kliknij tutaj, żeby przejść ; kliknij tutaj, żeby przejść

Język:

eng

Powiązania:

Optica Applicata ; Optica Applicata, Vol. 35, 2005 ; Optica Applicata, Vol. 35, 2005, nr 2 ; Politechnika Wrocławska. Wydział Podstawowych Problemów Techniki

Prawa:

Wszystkie prawa zastrzeżone (Copyright)

Prawa dostępu:

Dla wszystkich w zakresie dozwolonego użytku

Lokalizacja oryginału:

Politechnika Wrocławska